SiO2改性对紫外光固化木器涂料性能的影响(PDF)

《南京林业大学学报(自然科学版)》[ISSN:1000-2006/CN:32-1161/S]

Issue:
2014年04期
Page:
173-176
Column:
研究简报
publishdate:
2014-07-01

Article Info:/Info

Title:
Influence of modification of UV-curing wood coatings with SiO2 on its mechanical properties and gloss
Article ID:
1000-2006(2014)04-0173-04
Author(s):
YAN Xiaoxing WU Yan MAO Weiguo XU Wei
College of Furniture and Industrial Design,Nanjing Forestry University,Nanjing 210037, China
Keywords:
wood coatings UV-curing SiO2 coating mechanical properties gloss
Classification number :
TQ633
DOI:
10.3969/j.issn.1000-2006.2014.04.034
Document Code:
A
Abstract:
Influence of UV-curing wood coatings modification with SiO2 on its mechanical properties and gloss was investigated in this paper. UV curing wood coatings were modified by SiO2, and then the glossiness and mechanical properties including hardness, adhesion,resistance impact strength of film coating formed under the optimum modification conditions were tested. It was found that UV curing wood coatings had good hardness, adhesion and impact strength when the SiO2 content was 0.66%-1.32%, the dry time was 2 min and UV lamp was 3, but the mechanical properties of coatings decreased and their glossiness displayed matt when the SiO2 content was over 1.32%.

References

[1] Sabani S, Onen A H, Gungor A. Preparation of hyperbranched polyester polyol-based urethane acrylates and applications on UV-curable wood coatings[J]. Journal of Coatings Technology and Research, 2012, 9(6): 703-716.
[2] 毛卫国,闫小星,吴燕,等. CaCO3改性对UV固化木器涂料性能的影响[J]. 家具, 2013, 34(4): 26-29. Mao W G, Yan X X, Wu Y, et al. Performance of UV-curable wood coatings modified by CaCO3[J]. Furniture, 2013, 34(4): 26-29.
[3] 彭钧浪,刘志刚,罗先平,等. 低气味UV光固化木器涂料的制备[J]. 中国涂料, 2012, 27(2): 46-48. Peng J L, Liu Z G, Luo X P, et al. Preparation of low odor UV-curable woodenware coatings[J]. China Coatings, 2012, 27(2): 46-48.
[4] 郑建鹏,张军. 影响聚氨酯亚光清漆涂膜光泽稳定性的因素[J]. 中国涂料, 2008, 23(1): 23-25. Zheng J P, Zhang J. Influencing factors of film gloss stability of semi-gloss PU varnish[J]. China Coatings, 2008, 23(1): 23-25.
[5] Jancovicova V, Mikula M, Havlinova B, et al.Influence of UV-curing conditions on polymerization kinetics and gloss of urethane acrylate coatings[J]. Progress in Organic Coatings, 2013, 76(2-3): 432-438.
[6] 林晓峰,曾春龙. 100% UV固化涂料的最佳消光效应[J]. 涂料工业, 2005, 35(10): 13-17. Lin X F, Zeng C L. The most effective matting technology for 100% UV-curing coatings[J]. Paint & Coating Industry, 2005, 35(10): 13-17.
[7] Bardi M A G, Machado L D B. Accompanying of parameters of color, gloss and hardness on polymeric films coated with pigmented inks cured by different radiation doses of ultraviolet light[J]. Radiation Physics and Chemistry, 2012, 81(9): 1332-1335.
[8] 朱海龙,吴玉章,孙伟圣. 三聚氰胺脲醛树脂胶黏剂的合成[J]. 南京林业大学学报:自然科学版, 2013, 37(1): 173-176. Zhu H L, Wu Y Z, Sun W S. Synthesis of melamine-urea-formaldehyde resin adhesive[J]. Journal of Nanjing Forestry University:Natural Sciences Edition, 2013, 37(1): 173-176.
[9] Landrya V, Riedl B, Blanchet P. Nanoclay dispersion effects on UV coatings curing[J]. Progress in Organic Coatings, 2008, 62(4): 400-408.
[10] 章芬成,杨建军,吴庆云,等. 纳米SiO2改性醇溶性蓖麻油-聚氨酯树脂的制备与表征[J]. 精细化工,2012, 29(10): 1021-1025. Zhang F C, Yang J J, Wu Q Y, et al.Synthesis and characterization of alcohol-soluble polyurethane modified by castor oil and nano-SiO2[J]. Fine Chemicals, 2012, 29(10): 1021-1025.
[11] 顾凯,周晓燕. 纳米二氧化钛/三聚氰胺树脂混合体系的特性[J]. 南京林业大学学报:自然科学版, 2010, 34(2): 65-68. Gu K, Zhou X Y. Characteristics of nano-sized TiO2/melamine formaldehyde resin mixture[J]. Journal of Nanjing Forestry University:Natural Sciences Edition, 2010, 34(2): 65-68.
[12] 赖俊伟,杨建文,刘晓暄. 碳酸钙表面感光修饰及其在UV涂料中的应用[J]. 影像科学与光化学, 2013, 31(1): 10-17. Lai J W, Yang J W, Liu X X. Surface photosensitive modification of calcium carbonate and application in UV-curable coating[J]. Imaging Science and Photochemistry, 2013, 31(1): 10-17.
[13] 莫引优,陈奎,何其飞,等. 用二氧化硅聚氨酯涂料改良木材表面性质的研究[J]. 北京林业大学学报, 2012, 34(4): 154-159. Mo Y Y, Chen K, He Q F, et al. Modifying wood surface properties by SiO2 polyurethane coating[J]. Journal of Beijing Forestry University, 2012, 34(4): 154-159.
[14] Mirabedini S M, Mohseni M, PazokiFard S, et al. Effect of TiO2 on the mechanical and adhesion properties of RTV silicone elastomer coatings[J]. Colloids Surface A, 2008, 317(1-3): 80-86.
[15] Shum P W, Zhou Z F, Li K Y, et al. Mechanical and tribological properties of amorphous carbon films deposited on implanted steel substrates[J]. Thin Solid Films, 2004, 458(1-2): 203-211.
[16] 闫小星. 金属/聚氨酯红外低发射率复合涂层界面改性及性能研究 [D]. 南京: 南京航空航天大学, 2012. Yan X X. Interface modification and properties of metal/polyurethane infrared low emissivity composite coatings [D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2012.

Last Update: 2014-07-31