银改性六方介孔硅的合成及其抗菌性能研究(PDF)

《南京林业大学学报(自然科学版)》[ISSN:1000-2006/CN:32-1161/S]

Issue:
2009年02期
Page:
107
Column:
研究论文
publishdate:
2009-03-30

Article Info:/Info

Title:
Synthesis and antibacterial ability of silvercontaining hexagonal mesoporous silica
Author(s):
CHEN Junhua12 WANG Fei1* DING Zhijie2 CHEN Zhongping2 ZHANG Ping 2 FU Zaihui3
1.College of Chemical Engineering, Nanjing Forestry University, Nanjing 210037, China; 2.Chemistry Department, Anhui Science and Technology University, Fengyang 233100, China; 3.College of Chemistry and Chemical Engineering, Hunan Normal University, Chang
Keywords:
hexagonal mesoporous silica modification synthesis characterization antibacterial ability
Classification number :
O643
DOI:
10.3969/j.jssn.1000-2006.2009.02.026
Document Code:
A
Abstract:
Antibacterial material of silvercontaining hexagonal mesoporous silica (AgHMS) was synthesized using solgel method, and its structure and nature were characterized by means of XRD, FTIR, UVVis, ESEM, EDS, TGDTA and N2 absorptiondesorption technique. The antibacterial ability of the material was also investigated using turbidimetric method. The results indicated that the AgHMS material was thermostable, the particles of silver were embed and evenly distributed in the framework/nonframework. The crystallinity, mesoporous ordered degree and specific surface area changed then silver particles were added into the material. Both the template agent and demoulding temperature had notable effect on the peak position and strength in IR spectra of Si-O. The results of antibacterial experiments showed that AgHMS had strong inhibition on bacterial. It had an increase order to inhibit Staphylococcus aureus, Gemma bacillus, Escherichia coli and Bacillus subtilis. When the dosage of AgHMS was 0.20 mg/L, the growth of B.subtilis was inhibited. B.subtilis was almost completely killed after 12 hours when the dosage of AgHMS was up to 1.00 mg/L.

References

[1]程永清,李丽玲,尹晓敏,等. 溶胶凝胶法制备的掺银TiO2的相变和抗菌性能研究[J]. 贵金属,2007,28(1):37-42.
[2]汤戈,王振家. 无机抗菌材料的发展与应用[J]. 材料科学与工程,2002,20(2):298-301.
[3]Ganapati D Y, Haresh G M. Novelties of synthesis of acetoveratrone using heteropoly acid supported on hexagonal mesoporous silica[J]. Microporous and Mesoporous Materials, 2003, 63: 85-96.
[4]Yanyong L, Kazuhisa M, Megumn I, et al. Syntheses of Ti and Alcontaining hexagonal mesoporous silicas for gasphase epoxidation of propylene by molecular oxygen[J]. Applied Catalysis A: General, 2006, 309: 91-105.
[5]Muriel A E, Adam F L, Karaen W. High activity, templated mesoporous SO2+4/ZrO2/HMS catalysts with controlled acid site density for αpinene isomerisation[J]. Microporous and Mesoporous Materials, 2005, 80: 301-310.
[6]Ana R S, Karen W, James H C, et al. Covalent attachment of chirl manganese (Ⅲ) salen complexes onto functionalized hexagonal mesoporous silica and application to the asymmetric epoxidation of alkenes[J]. Microporous and Mesoporous Materials, 2006, 91: 128-138.
[7]YANG R T, Pinnavaia T J, Li W, et al. Fe3+ exchanged mesoporous AlHMS and AlMCM41 molecular sieves for selective catalytic reduction of NO with NH3[J]. J Catal, 1997, 172: 488-493.
[8]陈君华,伏再辉,尹笃林,等. 中孔CuHMS分子筛的合成[J]. 石油化工,2000,29(10):756-758.
[9]Tanev P T,Pinnavaia T J. A neutral templating route to mesoporous molecular sieves[J]. Science, 1995, 267: 865-867.
[10]Fu Z H, Chen J H, Chen Y D, et al. Highly effective CuHMS catalyst for hydroxylation of phenol[J]. Catal Lett, 2000, 66: 105-108.
[11]师进文,郭烈锦. Cr或V掺杂的HMS在甲酸溶液中的光催化产氢性能的研究[J]. 化学学报,2007,65 (4):323-328.
[12]薛松. 有机结构分析[M]. 合肥:中国科学技术大学出版社,2005.
[13]徐如人,庞文琴,于吉红,等. 分子筛与多孔材料化学[M]. 北京:科学出版社,2004.
[14]刘红,王志刚,李浩. FeMSU1介孔分子筛的合成及其催化苯酚羟基化性能[J]. 催化学报,2007,28(3):222-228.
[15]李吉东,李玉宝,王学江,等. 载铜锌纳米羟基磷灰石的抗菌性能及机理研究[J]. 无机材料学报,2006,21 (1):162-168.

Last Update: 2009-03-30