尾巨桉木材的渗透性对皱缩的影响(PDF)

《南京林业大学学报(自然科学版)》[ISSN:1000-2006/CN:32-1161/S]

Issue:
2010年05期
Page:
83-86
Column:
研究论文
publishdate:
2010-10-08

Article Info:/Info

Title:
Effect of the permeability of Eucalyptus urophylla×E.grandis wood on collapse in drying
Author(s):
MIAO Ping ZHANG Yaoli ZHUANG Shouzeng WANG Xiaomin CHEN Jiarong FAN Zhengzheng
College of Wood Science and Technology, Nanjing Forestry University, Nanjing 210037, China
Keywords:
Eucalyptus urophylla×E.grandis collapse permeability drying
Classification number :
S781.35
DOI:
10.3969/j.jssn.1000-2006.2010.05.018
Document Code:
A
Abstract:
In this paper the gas permeability of wet Eucalyptus urophylla×E.grandis wood was measured, drying tests were carried in several drying conditions and the collapse rule was observed, then the effect of the permeability of E.urophylla×E.grandis wood on collapse in drying was discussed. The test results showed the region of the easy collapse in transition from sapwood to heartwood, and the sapwood permeability was larger than the heartwood and the permeability decreased quickly from sapwood to heartwood. When the relative humidity was constant, the higher the temperature was, the greater the depth of shrinkage was. When the temperature was constant, the lower the relative humidity was, the greater the depth of shrinkage was. The small permeability in heartwood mainly was due to there were large tylosis in the vessels and vestured pit between the vessels. The reason of collapse in the wood was actions result of the compressing stress generated interior during wood drying and the smaller permeability caused greater capillary tension and the vapor partial pressure difference.

References

[1]Chafe S C. The distribution and interrelationship of collapse, volumetric shrinkage, moisture content and density in trees of Eucalyptus regnans F. Muell[J]. Wood Sci Tech, 1985, 19(4): 329-345. [2]Yany J L. An attempt to reduce collapse through introducing cell wall deformations[J]. Wood and Fiber Sci, 1998, 30(1): 81-90. [3]Stamm A J. Wood and Cellulose Science[M]. New York: The Ronald Press Company, 1964. [4]王喜明,王军,刘晓丽. 木材皱缩评价指标的研究[J]. 林业科学,2000,36(3):129-132. [5]江泽慧,费本华,王喜明,等. 尾巨桉木材木材干燥特性与工艺及其皱缩研究现状[J]. 木材工业,2002,16(4):3-6. [6]刘元. 木材干燥皱缩机理及其特性研究[J]. 中南林学院学报,1994,14 (2) :97-101. [7]庄寿增,赵寿岳,苗平. 木材皱缩现象中的力学问题探讨[J]. 北京林业大学学报,2005,27(S1):9-12. [8]Innes T C. Collapse and internal checking in the latewood of E ucalyptus regnans F. Muell[J]. Wood Sci Tech, 1996, 30: 373-383. [9]John F Siau. Wood: Influence of moisture on physical properties[R]. Virginia: Polytechnic Institute and State University, 1995.