Title:
Synthesis technology of bio-oil starch adhesive for interior plywood
Article ID:
1000-2006(2014)06-0121-04
Author(s):
ZHANG QiCHANG Jianmin*ZHANG Jizong
College of Materials Science and Technology,Beijing Forestry University,Beijing 100083,China
Keywords:
bio-oil starch adhesive synthesis technology
Classification number :
TQ433
DOI:
10.3969/j.issn.1000-2006.2014.06.023
Document Code:
A
Abstract:
Bio-oil, and starch were used as the main material for preparing environmental friendly and low price bio-oil starch adhesive(BOSA)which was applied in the preparation of interior plywood. Influence of the starch emulsion concentration, acrylamide content, ammonium sulfate and bio-oil content on the bonding strength, solid content and viscosity of BOSA were investigated, and the optimal preparation conditions were determined by orthogonal experiments. The results showed that the BOSA had best combination property, its bonding strength(1.44 MPa)could reach the national standard GB/T 9846—2004 of class Ⅲ plywood(≥0.7 MPa)requirement, and the storage life reached 15 days when mass fractions of the concentration of starch emulsion was 40%, ammonium sulfate content was 2.5%, acrylamide and bio-oil content were 20%.

References

[1] 罗发兴,黄强,杨连生.淀粉基胶粘剂研究进展[J].化学与粘合,2003(2):78-80. Luo F X, Huang Q, Yang L S. The study progress of starch adhesives[J]. Chemistry and Adhesion, 2003(2):78-80.
[2] 阎春绵,张忠厚,吴卫林,等.环保耐水型木材用胶粘剂的研究[J].中国胶粘剂,2008,17(7):1-5. Yan C M, Zhang Z H, Wu W L, et al. Study on environmental friendly and water-resistance adhesive for wood [J]. China Adhesives, 2008,17(7):1-5.
[3] 吴本刚,马海乐,何荣海,等.生物质胶黏剂的研究进展[J].林产工业,2011,38(4):8-11. Wu B G, Ma H L, He R H, et al. Advances in biomass adhesive research[J].China Forest Products Industry, 2011,38(4):8-11.
[4] 张继宗,张琪,常建民. 生物油淀粉胶黏剂制备工艺研究[J].现代化工,2013,33(6):62-67. Zhang J Z, Zhang Q, Chang J M.Preparation process of bio-oil starch adhesive[J]. Modern Chemical Industry, 2013,33(6):62-67.
[5] 高雪景,常建民,许守强,等.酚醛树脂用生物油反应活性的测试与分析[J].中国胶粘剂,2012,21(5):5-8. Gao X J, Chang J M, Xu S Q, et al.Testing and analysis of reactivity of bio-oil for phenolic resin [J]. China Adhesives, 2012,21(5):5-8.
[6] Mourant D,Yang D Q,Roy C.Decay resistance of pf-pyrolytic oil resin-treated wood[J].Forest Products Journal,2007,57(5):30-35.
[7] 沈哲红,方群,叶良明,等. 竹醋液制剂的抑菌性及其竹材防霉性评价[J].木材工业,2009,23(6): 37-45. Shen Z H, Fang Q, Ye L M, et al.Bamboo vinegar antifungal performance and mold inhibition[J]. China Wood Industry, 2009,23(6): 37-45.
[8] 沈哲红,方群,鲍滨福,等.竹醋液及竹醋液复配制剂对木材霉菌的抑菌性[J].浙江林学院学报,2010,27(1): 99-104. Shen Z H, Fang Q, Bao B F, et al.Antifungal characteristics of raw bamboo vinegar and bamboo vinegar preparations on wood mold[J]. Journal of Zhejiang Forestry College, 2010,27(1):99-104.
[9] 刘景宏,林巧佳,杨桂娣.改性淀粉胶黏剂的研制[J].木材工业,2004,18(4): 8-11. Liu J H, Lin Q J, Yang G D.Study on modifying starch adhesive for plywood manufacturing [J]. China Wood Industry, 2004,18(4): 8-11.
[10] 陈士英,曹志强,李亚兰,等.GB/T 17657—1999 人造板及饰面人造板理化性能试验方法[S].北京:中国标准出版社,1999.
[11] 高振忠,陈绍荣,黄志平,等.GB/T 14074—2006 木材胶粘剂及其树脂检验方法[S]. 北京:中国标准出版社,2006.
[12] Kamke F A, Lee J N. Adhesive penetration in wood-A review [J]. Wood and Fiber Science,2007,39(2):205-220.
[13] 叶楚平,王念贵. 丙烯酸系共聚物改性玉米淀粉胶粘剂[J]. 粘接,2002,23(1):26-28. Ye C P, Wang N G.Development of acrylic copolymer modified corn starch-based corrugated paperboard adhesive[J]. Zhan Jie, 2002,23(1):26-28.
[14] 曹忠荣,张莺红,康熹,等.GB/T 9846—2004 胶合板[S]. 北京:中国标准出版社,2004.

Last Update: 2014-12-31