为了使竹木复合层合板能够更好地应用于公交车底板，对该产品进行了50万次动态弯曲、45 万次动态扭转和3 000 km可靠性路面疲劳试验测试，观测板材的力学损耗及受破坏情况，并且对经 疲劳试验后的产品进行了弯曲力学性能测试。结果表明：经过50万次弯曲试验后，板材的各项弯曲 力学性能保留率均在90 %以上；45万次扭转试验后各项弯曲力学性能保留率在85 %以上；模拟装载 进行3 000 km可靠性路面试验后各项弯曲力学性能保留率在80 %以上。
Abstract
In order to get the better usage of bamboo/wood composited panel for bus floor, a series of performance tests for the composited panel including 500 000 times dynamic bending, 450 000 times dynamic torsion, and 3 000 km reliable running were carried out for observing its mechanical loss and damage status. Tests results indicated that the bending strength of the composited panel could still remain more than 90 %, 85 % and 80 %, respectively after the aforesaid dynamic bending, dynamic torsion and reliable running.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1]吴彩东,韩健,刘明彬. 新型竹木复合板的研制[J]. 林业科技开发,2007,21(3):64-66.
[2]喻云水. 竹木复合胶合板二次覆面工艺研究[J]. 林业科技,2005,30(6):40-42.
[3]曹平祥,郭晓磊,李四九,等. 新型竹木复合地板的热压工艺及其对质量的影响[J]. 木材工 业,2008,22(1):37-39.
[4]张晓冬,李君,王泉中,等. 竹木复合层合板力学性能预测与分析[J]. 南京林业大学学报:自然科 学版,2005,29(6):103-105.
[5]韩健. 定向竹木复合板表观弹性模量预测模型的构建[J]. 南京林业大学学报:自然科学 版,2009,33(1):33-36.
[6]朱一辛,关明杰,饶文彬,等. 木竹重组材抗弯性能的研究[J]. 南京林业大学学报:自然科学 版,2004,28(4):59-61.
[7]关明杰,朱一辛,张晓冬,等. 湿热条件对木竹复合胶合板弯曲性能的影响[J]. 南京林业大学学报 :自然科学版,2005,29(6):106-108.
[8]王戈,江泽慧,于文吉. 毛竹、杉木层积复合材弯曲与剪切破坏的微观形变过程[J]. 东北林业大 学学报,2008,36(2):27-29.
基金
收稿日期：2009-10-15修回日期：2010-04-26基金项目：国家高技术研究发 展计划(2002AA245171)作者简介：张晓冬(1962—),副教授。 Email: zhangxiaodong@njfu.com.cn。引文格式：张晓冬,程秀才,班磊. 竹木复合层合板抗疲劳性能的实验 研究[J]. 南京林业大学学报:自然科学版,2010,34(4):42-44.
PDF(416736 KB)