原胶是一种以聚异戊二烯为主要成分的天然高分子化合物，有良好的黏接性能，但价格较高，快干性不佳，加入改性松香可以解决此问题。利用硝酸、季戊四醇、丙烯酸丁酯、桐油等对松香进行改性，再加入乳化剂制成硝酸氧化松香水分散液。通过热分析、红外光谱分析，以及拉伸性能、快干性等测试，表明所合成的硝酸氧化松香水分散液的性能优于市售改性松香，可以代替部分原胶，而不影响其黏接性能，从而降低了产品成本，提高了快干性，达到了改性的目的。
Abstract
The original gum, which is a natural polymer component of polyisoprene. It has good adhesion properties. Modified rosin is used to reduce it’s cost and increase it’s quickdrying. The nitric acid, pentaerythritol, butyl acrylate, wood oil and etc. were used to modify rosin. Then add emulsifier to make rosin dispersion oxidized by nitric acid. At last through the thermal analysis , IR, the stretch performance test, the quickdrying test and so on. The results showed that the modified rosin dispersion had better performances than market modified rosin. It could partly take place of the original gum, but not affected the adhesion properties, so reduce costs and increase quickdrying, achieve the purposes of the modification.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1]任天瑞,李永红. 松香化学及其应用[M]. 北京:化学工业出版社,2003. [2]叶楚平,李陵岚,王念贵. 天然胶黏剂[M]. 北京:化学工业出版社,2003. [3]李佶辉,哈成勇. 松香改性的研究进展[J]. 天然产物研究与开发,2003,15(6):552-558. [4]曹祺风,宋文生,朱长春,等. 松香改性研究概述[J]. 广州化工,2007,35(5):10-12. [5]Armando J D Silvestre, Alessandro Gandini. Rosin: major sources, properties and applications[J]. Monomers, Polymers and Composites from Renewable Resources, 2008, 6: 67-88. [6]温佩,武文洁,赵小华. 美国松香改性产品及其应用的专利进展[J]. 化工技术与开发,2007,36(7):14-19. [7]丁霞. 松香衍生物的合成、结构表征及生物活性研究[D]. 南京:南京林业大学,2006. [8]刘祖光,雷福厚,安鑫南,等. 功能基聚氧化松香二元醇酯的制备与性能研究[J]. 福建林业科技,2008,35(2):119-125. [9]刘祖光,雷福厚,安鑫南. 松香的硝酸开环氧化[J]. 浙江林业科技,2008,28(1):5-9. [10]国家技术监督局.GB/T 8146—2003松香试验方法[S]. 北京:中国标准出版社,2003. [11]姚映钦. 有机化学[M]. 武汉:武汉理工大学出版社,2004. [12]张向宇. 胶黏剂分析与测试技术[M]. 北京:化学工业出版社,2004.
基金
收稿日期：2010-01-25修回日期：2010-04-08作者简介：朱岩(1963—)，教授，博士。Email: renyingwhut@163.com。引文格式：朱岩,任莹,陈国灿. 硝酸氧化松香水分散液的合成及其性能研究[J]. 南京林业大学学报:自然科学版,2010,34(5):101-104.
PDF(782405 KB)