以慈竹制作的重组竹为研究对象,对重组竹抗压与抗拉力学性能进行了研究,并将重组竹与落叶松等6种木材的力学性能 进行了比较。结果表明:重组竹顺纹抗拉强度为248.15 MPa,顺纹抗压强度129.17 MPa,稳定性能较好。通过与落叶松、云杉等 木材比较发现,重组竹的抗压和抗拉强度较高,纵向与横向抗压强度差异较小,EL/ET 比值小,不同方向的泊松比和强重比也有差别。重组竹的横纹抗压过程分为3个阶段(弹性阶段、塑性阶段、破坏阶段),最后发 生塑性破坏。
Abstract
By taking recombinant bamboo made of Neosinocalamus affinis as the research object, the tensile and compressive properties of recombinant bamboo were studied. The results were compared with six wood species including dahurian larch. The results showed that tension strength parallel to grain and compression strength parallel to gain of recombinant bamboo were 248.15 MPa and 129.17 MPa respectively, and the properties of which were stable. Compared with dahurian larch and spruce etc, the compression and tension strength of recombinant bamboo were higher, while difference between strength in transverse and longitudinal direction was much smaller,EL/ET were smaller, the Poisson’s ratio and strength weight ratio varied in directions. The curve of compressing perpendicular to grain was divided into three parts(elastic stage, plastic stage and failure stage), and it was plastic failure in the end.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 中华人民共和国国土资源部.耕地占补平衡考核办法[J].国土资源通讯,2006(13):9-10.
[2] 刘一星,赵广杰.木质资源材料学[M].北京:中国林业出版社,2004.
[2] 单炜,李玉顺.竹材在建筑结构中的应用前景分析[J].森林工程,2008,24(2):62-65.
[4] 李明,郑靓.竹材在建筑工程中的应用[J].广东建材,2011(2):23-26.
[5] 吴岩,李玉顺,葛贝德,等.改性竹材的应用与前景森林工程[J].森林工程,2008,24(6):68-71.
[6] 关明杰,林举媚,朱一辛.家具用重组竹干缩与湿胀性能研究[J].竹子研究汇刊,2009,28(3):38-41.
[7] 汪孙国,华毓坤.重组竹制造工艺的研究[J].木材工业,1991,5(2):14-18.
[8] 李琴,汪奎宏,杨伟明,等.重组竹材胶合板制造技术的研究[J].竹子研究汇刊,2003,22(4):56-60.
[9] 刘柏平,程万里,周建波,等.弧形原态重组竹制造工艺的初步研究[J].木材加工机械,2009,20(6):31-34.
[10] 程亮,王喜明,余养伦.浸胶工艺对绿竹重组竹材性能的影响[J].木材工业,2009,23(3):16-19.
[11] 汪孙国,华毓坤.软化工艺条件对竹材及其重组材性能的影响[J].南京林业大学学报,1994,18(1):57-62.
[12] 叶良明,姜志宏,叶建华,等.重组竹板材的研究[J].浙江林学院学报,1991,8(2):133-140.
[13] 孟凡丹,于文吉,陈广胜.四种竹材人造板的制造方法和性能比较[J].木材加工机械,2011,22(1):32-35.
[14] 关明杰,朱一辛,张心安.重组木与重组竹抗弯性能的比较[J].东北林业大学学报,2006,34(4):7,21.
[15] ZHU Rong-xian,YU Wen-ji. Effect of density on physical and mechanical properties of reconstituted small -sized bamboo fibrous sheet composite[J]. Advanced Materials Research, 2011,150-151:634-639.
[16] Qin L, YU W J. Research on surface color, properties of thermo-treated reconstituted bamboo lumber after artificial weathering test[J]. Advanced Materials Research, 2009,79-82:1395-1398.
[17] 全国木材标准化技术委员会.GB/T 1939—2009木材横纹抗压试验方法[S].北京:中国标准出版社,2009.
[18] 全国木材标准化技术委员会.GB/T 1938—2009木材顺纹抗拉强度试验方法[S].北京:中国标准出版社,2009.
[19] 全国木材标准化技术委员会.GB/T 1935—2009木材顺纹抗压强度试验方法[S].北京:中国标准出版社,2009.
[20] 全国木材标准化技术委员会.GB/T 1943—2009木材横纹抗压弹性模量测定方法[S].北京:中国标准出版社,2009.
[21] 成俊卿.木材学[M].北京:中国林业出版社,1985.
[22] 潘景龙,祝恩淳.木结构设计原理[M].北京:中国建筑工业出版社,2009.
[23] 尹思慈.木材学[M].北京:中国林业出版社,1996.
基金
收稿日期:2012-01-17 修回日期:2012-04-19 基金项目:国家林业公益性行业科研专项项目(201004005,200904034) 第一作者:张俊珍,硕士生。*通信作者:赵荣军,副研究员,E-mail: rongjun@caf.ac.cn。引文格式:张俊珍,任海青,钟永,等. 重组竹抗压与抗拉力学性能的分析[J]. 南京林业大学学报:自然科学版,2012,36 (4):107-111.
PDF(614244 KB)