通过自制的碱浸渍扩散装置对杨木横向碱浸渍扩散过程进行了研究。原料微观结构电镜分析发现,杨木边材的浸渍扩散性能优于心材。浸渍实验表明,杨木横向碱浸渍扩散过程可分为反应主导、反应与扩散并存、扩散主导3个阶段; 同时,通过单因素实验分析了温度、NaOH浓度、试样厚度、试样含水率等4个因素对碱浸渍扩散过程的影响。结果表明,温度与厚度对碱浸渍过程影响最大,NaOH浓度对与浸渍反应过程紧密相关的拐点值有一定影响,而含水率对碱浸渍扩散过程影响较小,但含水率饱和条件下的拐点值明显低于非饱和条件下的拐点值。
Abstract
The transverse alkali impregnating diffusion of poplar was studied with the self-made equipment. According to the scanning electron microscopy(SEM)analysis of the microstructure of raw material, impregnating diffusion performance of sapwood was better than the performance of heartwood. It was showed that there were three stages in the process of the transverse alkali impregnating diffusion of poplar, namely reaction-driven stage, reaction and diffusion coexistence stage and diffusion-driven stage. Meantime, the effects of main factors, which included temperature, concentration of NaOH, thickness of sample and moisture of sample, were investigated. The results showed that temperature and thickness of sample had significant effects on the alkali impregnating diffusion process. While, the concentration of NaOH influenced the inflection point mainly which had close link with reaction rate in the impregnating process. The moisture of sample had not remarkable influence on the process. But the inflection point value of water saturated sample was higher than that of water unsaturated samples in the moisture factor experiment.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] 李永峰,刘一星,于海鹏,等. 木材流体渗透理论与研究方法[J]. 林业科学,2011,47(2):134-144.Li Y F, Liu Y X, Yu H P, et al. Theory of fluids penetrating wood and its researching method [J]. Scientia Silvae Sinicae, 2011, 47(2):134-144.
[2] Sergey Malkov, Panu Tikka, Johan Gullichsen. Towards complete impregnation of wood chips with aqueous solutions Part 1:A retrospective and critical evaluation of the penetration process[J]. Paperi ja Puu, 2003, 85(8):460-466.
[3] João P F Simão, Ana P V Egas, M Gra a Carvalho, et al. Heterogenous studies in pulping of wood:Modelling mass transfer of alkali [J]. Chemical Engineering Jurnal, 2008, 139(3):615-621.
[4] Zanuttini M, Citroni M, Marzocchi V, et al. Alkali impregnation of hardwood chips[J]. TAPPI J, 2005, 4(2):28-30.
[5] Zanuttini M, Citroni M, Marzocchi V, et al. Alkali impregnation of hardwoods. Part 1:moderate treatment of poplar wood [J]. Journal of Pulp Paper Science, 2003, 29(9):313-317.
[6] 侯祝强,庄作峰. 木材流体渗透性研究的发展与趋势[J]. 世界林业研究,1999,12(1):33-37.Hou Z Q, Zhuang Z F. The development and tendency in the research on fluid permeability of wood [J]. World Forestry Research, 1999, 12(1):33-37.
[7] Philip F. Schneider. Pressure measurement in wood as a method to understand impregnation processes: conventional and supercritical carbon dioxide [D]. Oregon:Oregon State University, 1999.
[8] Bramhall G. The validity of Darcy’s law in the axial permeability of wood [J]. Wood Sci Technol, 1971, 5(2):121-134.
[9] 彭万喜,李凯夫,张党权. 木材渗透性研究的现状与趋势[J]. 木材工业,2004,18(5):8-10.Peng W X, Li K F, Zhang D Q. Review of research on wood permeability [J]. China Wood Industry, 2004, 18(5):8-10.
[10] Petty J A. Permeability and structure of the wood of sitka spruce [J]. Proc Roy Soc Lond, 1970, 175(1039):149-166.
[11] Petty J A. Fluid flow through the vessels of birch wood [J]. Journal of Experimental Botany, 1978, 29(16):1463-1469.
[12] Comstock G L. Longitudinal permeability of wood to galses and non-swelling liquids [J]. Journal of Forest Product, 1967, 17(10):41-46.
[13] Comstock G L. Directional permeability of softwoods [J]. Wood Fiber, 1970, 1(4):283-289.
[14] 鲍甫成,侯祝强. 针叶树材纵向气体渗透的三维流阻网络[J]. 林业科学,2002,38(4):111-116.Bao F C, Hou Z Q. The three-dimensional flow-resistor network for longitudinal gas permeability of softwoods [J]. Scientia Silvae Sinicae, 2002, 38(4):111-116.
[15] 侯祝强,鲍甫成. 针叶树材径向和弦向气体渗透的三维流阻网络[J]. 林业科学,2002,38(6):93-98.Hou Z Q, Bao F C. The three-dimensional flow-resistor network for radial and tangential gas permeability of softwoods [J]. Scientia Silvae Sinicae, 2002, 38(6):93-98.
[16] Sergey Malkov, Panu Tikka, Johan Gullichsen. Towards complete impregnation of wood chips with aqueous solutions. Part 2. Studies on water penetration into softwood chips [J]. Paperi ja Puu-Paper and Timber, 2001, 83(6):468-473.
[17] Vicente Costanza, Pedro Costanza. Estimating pure contributions in alkaline pulping processes [J]. Latin American Applied Research, 2002, 32:151-159
[18] 夏清,陈常贵. 化工原理:下册[M]. 天津: 天津大学出版社,2006.
[19] Chen D, Zhao J, Berk D, et al. A method for measuring pulping liquor penetration into wood structure [J]. Cellulose Chem Technol, 2010, 44(9):319-325.
[20] Magnus T rnqvist, Tapio Hurme, Jarl B. Rosenholm. Drift speed:a way of measurding diffusion and tortuosity of porous materials [J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2001, 180:23-31.
[21] 鲍甫成,吕建雄. 木材渗透性可控制原理研究[J]. 林业科学,1992,28(4):336-342.Bao F C, Lv J X. A study of the principle of permeability control of wood [J]. Scientia Silvae Sinicae, 1992, 28(4):336-342.
基金
收稿日期:2013-01-21 修回日期:2013-06-06
基金项目:东北林业大学研究生科技创新项目(STIP10)
第一作者:王永贵,硕士。*通信作者:岳金权,副教授。E-mail: yuejinq@163.com。
引文格式:王永贵,岳金权. 杨木横向碱浸渍扩散的研究[J]. 南京林业大学学报:自然科学版,2014,38(1):103-109.
PDF(2313482 KB)