采用微观数字散斑干涉技术和宏观剪切强度试验相结合,分析并讨论了杨木单板背面裂隙的存在对其胶合界面微观力学性能和宏观剪切强度的影响; 采用淀粉糊、淀粉糊/木粉、豆胶3种封闭剂处理杨木胶合界面上的背面裂隙,探讨改性试样微观应变分布和宏观力学性能之间的关联。结果表明:存在背面裂隙的杨木单板胶合界面上的应变数值较大,达到1.5×10-3～4.0×10-3,复合材料整体的强度显著减小; 不同封闭剂处理背面裂隙的试件,其胶合界面的应变显著大于未处理的试件; 封闭剂处理后,杨木单板层积材干强度未能全部提高,湿强度却出现不同程度的下降。
Abstract
Influence of lathe checks on microscopic mechanical properties of poplar veneer bonding interface and macroscopic shear strength was examined by using microscopic digital speckle pattern interferometry combined with macroscopic shear testing in this paper. In addition, gelatinized starch, gelatinized starch/wood flour compound, soybean adhesive were used to modify lathe checks of poplar bonding interface, and the relationship of microscopic strain distribution and macroscopic mechanical properties of modified samples was discussed. The results showed that the strain values of bonding interface with lathe checks were bigger at the value of 1.5×10-3-4.0×10-3, and the whole composite strength decreased significantly. The strain values of bonding interface modified by different sealing treatment were remarkably bigger than unmodified samples, at the same time, not all dry shear strength increased while all wet shear strength deceased to varying degree.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1] Faust T D, James T Rice. Characterizing the roughness of southern pine veneer surfaces[J]. Forest Prod J, 1986, 36(11/12):75-81.
[2] Koch P. Effects of seven variables on properties of southern pine plywood:Part I,maximizing wood failure[J]. Forest Prod J, 1965, 15(9):335-361.
[3] Cumming J D, Fischer C, Dickinson F E. Rotary veneer cutting characteristics of young-growth redwood[J]. Forest Prod J, 1969, 19(11):26-30.
[4] Palka L C, Holmes B. Effect of log diameter and clearance angle on the peel quality of 0.125-inch-thick Douglas-fir veneer[J]. Forest Prod J, 1973, 23(7):33-41.
[5] 顾国庆,王开福.物体变形测量的相移数字散斑剪切干涉术[J].激光杂志,2011,32(4):16-17.Gu G Q, Wang K F. Digital phase-shifting shearography for measurement of object deformation[J]. Laser Journal, 2011,32(4):16-17.
[6] 米红林,方如华.电子散斑干涉法在研究双材料界面力学行为中的应用[J].力学季刊,2005,26(1):14-19.Mi H L, Fang R H. Study of bimaterial interfacial mechanical behavior by electronic speckle pattern interferometry[J]. Chinese Quarterly of Mechanics, 2005,26(1):14-19.
[7] Valla A, Konnerth J, Keunecke D, et al. Comparison of two optical methods for contactless, full field and highly sensitive in plane deformation measurements using the example of plywood[J]. Wood Sci Technol, 2011(45): 755-765.
[8] 孙艳玲,赵东,高继河.数字散斑相关方法在木材断裂力学上的应用分析[J].北京林业大学学报, 2009,31(1):206-209.Sun Y L, Zhao D, Gao J H. Application of digital speckle correlation method in wood fracture mechanic[J]. Journal of Beijing Forestry University,2009,31(1): 206-209.
[9] 徐曼琼,金观昌,鹿振友.数字散斑面内相关法测量木材抗压弹性模量[J].林业科学,2003,39(2):174-176.Xu M Q, Jin G C, Lu Z Y. Digital spackle correlation method(DSCM)for measurement of wood compresson elastic modulus[J]. Scientia Silvae Sinicae,2003,29(2):174-176.
[10] 江泽慧,费本华,张东升,等.数字散斑相关方法在木材科学中的应用及展望[J].中国工程科学,2003,5(11):1-7.Jiang Z H, Fei B H, Zhang D S, et al. Application and prospect of digital speckle correlation method on wood science[J]. Engineering Science, 2003,5(11):1-7.
[11] 关明杰,王路,常馨曼. 杨木/酚醛树脂胶合界面相的荧光跟踪解析[J]. 南京林业大学学报:自然科学版,2013,37(5):125-128.Guan M J, Wang L, Chang X M.Fluorescence tracking analysis of poplar and phenol-formaldehyde bonding interface[J]. Journal of Nanjing Forestry University:Natural Sciences Edition, 2013, 37(5):125-128.
[12] Wang L, Guan M J. Influence of veneers’ lathe checks on strain distribution at wood-adhesive interphase measured by Electronic Speckle Pattern Interferometry(ESPI)[C]//Beijing:55th SWST International Convention, 2012.
[13] 单辉祖,谢传锋.工程力学[M].北京:高等教育出版社,2006.
[14] Wescott J M, Frihart C R. Competitive soybean flour/phenol-formaldehyde adhesives for oriented strand board[C]//Pullman WA:38th International Wood Composites Symposium, 2004.
[15] Veigel S, Müller U, Keckes J, et al. Cellulose nanofibrils as filler for adhesives: effect on specific fracture energy of solid wood-adhesive bonds[J]. Cellulose, 2011(18):1227-1237.
[16] Turunen M, Alvila L, Pakkanen T T, et al. Modification of phenol-formaldehyde resol resins by lignin, starch, and urea[J]. J Appl Polym Sci, 2003(88):582-588.
基金
收稿日期:2014-02-19 修回日期:2014-04-08
基金项目:江苏省自然科学基金项目(BK2011822); 江苏高校优势学科建设工程资助项目(PAPD); 苏北科技发展计划:科技型企业技术创新项目(BC2013425)
第一作者:关明杰,副研究员。E-mail:mingjieguan@126.com。
引文格式:关明杰, 雍宬,王路. 背面裂隙对杨木胶合界面力学性能的影响[J]. 南京林业大学学报:自然科学版,2014,38(5):15-19.
PDF(2088554 KB)