以去金属离子处理后的漂白硫酸盐桉木浆及针叶木浆为原料，研究纸浆纤维对Ca2+的吸附动力学及影响吸附的因素。结果表明：Ca2+初始浓度较低时，漂白化学木浆对Ca2+的吸附能力随着Ca2+初始浓度的增加而快速提高。Ca2+初始浓度0.471 7 mmol/L时，阔叶木浆达到饱和吸附，吸附量为0.016 0 mmol/g；针叶木浆在Ca2+初始浓度为0.220 1 mmol/L时就达到饱和吸附，吸附量为0.008 4 mmol/g，吸附能力与针阔叶浆各自所带羧基量一致。在pH 7.5、温度25 ℃条件下，符合Langmuir方程等温吸附线，且纸浆对Ca2+的吸附为单分子吸附。Ca2+浓度和pH的升高将使纸浆纤维对Ca2+的吸附能力提高，阔叶木浆和针叶木浆中Ca2+加入量为0.035 6和0.016 5 mmol/g时，木浆达到饱和吸附。pH超过7，纸浆表面游离羧基将完全被Ca2+吸附；纸浆纤维对Ca2+的吸附属放热吸附，提高温度将会降低纸浆纤维对Ca2+的吸附量。关键词：化学木浆；Ca2+；吸附动力学
Abstract
The adsorbing kinetics and the factors of influencing calcium ion adsorption of both deionized BKP hard wood pulp and soft wood pulp were studied in this paper. The results showed that the adsorption capability of pulp fiber rise along with the augment of the beginning consistency of Ca2+ at a low Ca2+ consistency. The saturation adsorption capability of hard wood pulp is 0.016 0 mmol/g at the content of Ca2+ 0.471 7 mmol/L, and the soft wood pulp being 0.008 4 mmol/g at the content of Ca2+ 0.220 1mmol/L, which accords with the carboxyl content of pulps. At the conditions of pH 7.5 and 25 ℃, ce/Q and ce keep excellent linearity relationship, the R2 being respectively 0.95 and 0.99. It indicates the adsorption between pulp fiber and Ca2+ is chemistry adsorption, which accords with Langmuir isothermal equation, also belongs to single molecular adsorption. The adsorption capacity of chemical wood pulp fiber on Ca2+ rise along with pH or content of Ca2+, and the saturated adsorption content of Ca2+ of both BKP hard wood pulp and BKP soft wood pulp is 0035 6 mmol/g and 0.016 5 mmol/g, the pulp being entirety saturated adsorption with Ca2+ after pH 7. Arising temperature will low the adsorption capacity, which belongs to exothermic adsorption between pulp fibers and Ca2+.
{{custom_sec.title}}
{{custom_sec.title}}
{{custom_sec.content}}
参考文献
[1]Pancha P B. Closure of mill whitewater systems reduces water use, conserves energy[J]. Pulp&Paper, 1992, 66(3): 57-60.
[2]Strutz M D, Springer A M. A wetend optimization strategy for total water reuse[J]. Tappi J, 1982, 65(3): 139-142.
[3]Hulkko V M, Deng Y. Effects of watersoluble inorganic salts and organic materials on the performance of different polymer retention aids[J]. Journal of Pulp and Paper Science, 1999, 25(11): 378-383.
[4]Li Shan, Dai Hongqi. Study on the influences of inorganic salts on WRV of papermaking stock[C]//2nd ISTPPBFP, Nanjing, 2004.
[5]Dobbins R J, Alexader S D. The physical and optical properties of paper made at high salt concentrations[J]. Tappi J, 1977, 60(12): 117-120.
[6]Leo N. Papermaking chemistry[M]. New York: Published by FPEA and TAPPI, 2000.
[7]何北海,何滢滢. 造纸清洁生产与系统水封闭回用——造纸生产水系统封闭与“零排放”探讨之一[J]. 中国造纸,2000(5):43-48.
[8]何北海,文飚,刘焕彬. 清洁生产与纸机湿部化学系统的适应性——造纸生产水系统封闭与“零排放”探讨之二[J]. 中国造纸,2000(6):47-52.
[9]叶春洪. ACS对造纸湿部系统钙离子的络合作用及机理研究[D]. 南京:南京林业大学,2008.
[10]Isbister R. The closed cycle concept Kraft mill at great lakes, an advanced status report[J]. Pulp and Paper Canada, 1979: 121-130.
[11]南京林业大学. 木材化学[M]. 北京:中国林业出版社,1987.
[12]刘温霞. 造纸湿部化学[M]. 北京:化学工业出版社,2006.
[13]石淑兰. 制浆造纸分析与检测[M]. 北京:中国轻工业出版社,2003..
[14]刘丽莎. 漂白桉木浆细小纤维表面化学特性研究[D]. 南京:南京林业大学,2006.
[15]李青燕. 多孔多胺化交联壳聚糖的合成及其对重金属离子的吸附性能研究[D]. 北京:北京工业大学,2003.
[16]曲荣君. 新型螯合树脂的设计、合成及性能研究[D]. 天津:天津大学,2002.
[17]赵振国. 吸附作用应用原理[M]. 北京:化学工业出版社,2005.
[18]何曼君. 高分子物理[M]. 3版. 上海:复旦大学出版社,2007.
[19]范康年. 物理化学[M]. 北京:高等教育出版社,2005.
[20]Drew Myers. 表面、界面和胶体—原理和应用[M]. 吴大诚,译. 北京:化学工业出版社,2004.
[21]徐寿昌. 有机化学[M]. 北京:高等教育出版社,1993.
[22]Chen Yanxiao, Wang Gongying. Adsorption properties of oxidized carboxymethyl starch and crosslinked carboxymethyl starch for calcium ion[J]. Colloids and Surface A, 2006, 289: 75-83.
基金
收稿日期：2009-02-22修回日期：2009-09-02基金项目：国家自然科学基金项目(30871995)；江苏省属高校自然科学重大基础研究项目(09KJA220002)；江苏省制浆造纸科学与技术重点实验室课题(200818)作者简介：王忠良(1969—)，讲师，博士生。*戴红旗(通信作者)，教授。Email: daihq@njfu.com.cn。引文格式：王忠良,叶春洪,戴路,等. 纸浆纤维对钙离子吸附行为及机理[J]. 南京林业大学学报:自然科学版,2010,34(1):59-63.