Study on the characteristics of bamboo charcoal modified with nitric acid

doi:10.3969/j.jssn.1000-2006.2012.02.004

JOURNAL OF NANJING FORESTRY UNIVERSITY ›› 2012, Vol. 36 ›› Issue (02): 15-21.doi: 10.3969/j.jssn.1000-2006.2012.02.004

Previous Articles Next Articles

Study on the characteristics of bamboo charcoal modified with nitric acid

WU Guangqian¹,SUN Xinyuan²,ZHONG Liyun¹,ZHANG Qisheng^1*

1.College of Wood Science and Technology, Nanjing Forestry University, Nanjing 210037, China; 2.Nanjing CEC Environmental Protection Co., Ltd.,Nanjing 211102, China

Online:2012-04-10 Published:2012-04-10

Abstract

Abstract: Nitric acid with different concentrations(17%, 34%, and 68% respectively)was employed to modify the bamboo charcoal, and the iodine value, ash and water content of raw and modified bamboo charcoal samples were measured. Test results showed that the iodine value and ash content of three kinds of modified bamboo charcoal decreased slightly, while the water content of three kinds of modified bamboo charcoal samples increased sharply, the bamboo charcoal sample modified with 68% nitric acid has the most remarkable change of these above values. The Boehm titration,FTIR,BET,SEM-EDS and TG-DSC were used to characterize raw and modified bamboo charcoal samples. The results showed that the amount of different kinds of oxygen-containing groups increased on the surface of modified bamboo charcoal samples, while the carbon content decreased evidently,the surface of modified bamboo charcoal became more tough than the raw bamboo charcoal, and the slope of weight loss curves of modified bamboo charcoal were more successive and steeper than that of the raw bamboo charcoal,which showed that a great number of H₂O molecules and surface functional groups were formed on the surface of modified bamboo charcoal.

CLC Number:

TQ424

WU Guangqian,SUN Xinyuan,ZHONG Liyun,ZHANG Qisheng. Study on the characteristics of bamboo charcoal modified with nitric acid[J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2012, 36(02): 15-21.

References

[1] 朱江涛,黄正宏,康飞宇,等.竹炭的性能和应用研究进展[J].材料导报,2006,20(4):41-43,52.
[2] 张文标,叶良明.竹炭的生产和应用[J].竹子研究汇刊,2001,20(2):48-53.
[3] Kei M, Toshitatsu M, Yasuo H, et al. Removal of nitrate-nitrogen from drinking water using bamboo powder charcoal[J]. Bioresource Technology, 2004, 95(3): 255-257.
[4] Wang S Y, Tsai M H, Lo S F, et al. Effects of manufacturing conditions on the adsorption capacity of heavy metal ions by Makino bamboo charcoal[J]. Bioresource Technology, 2008, 99(15): 7027-7033.
[5] Chun Y Y, Mohd K A, Wan M A, et al. Review of modification of activated carbon for enhancing contaminant uptake from aqueous solutions[J]. Separation and Purification Technology, 2007,52(3): 403-415.
[6] Santiago M, Stuber F, Fabregat A, et al. Modified activated carbons for catalytic wat air oxidation of phenol[J]. Carbon, 2005, 43(10): 2134-2145.
[7] Hajime Tamon, Morio Kazaki. Influence of acidic surface ofides of activated carbon on gas adsorption characteristics[J]. Carbon, 1996, 34(6): 741-746
[8] Monser L, Adhoum N. Modified activated carbon for the removal of copper, zinc, chromium and cyanide from wastewater [J]. Separation and Purification Technology, 2002, 26(2):137-146.
[9] Boehm H P. Some aspects of the surface chemistry of carbon black and other carbons[J].Carbon, 1994,32(5): 759-769.
[10] 孙新元.表面改性竹炭对微污染水中有机物的吸附[D].南京:南京林业大学,2010.
[11] 张巍,应维琪,常启刚,等.水处理活性炭吸附性能指标的表征与应用[J].中国环境科学,2007,27(3):289-294.
[12] 高尚愚,周建斌,左宋林,等.碘值、亚甲基蓝及焦糖脱色力与活性炭孔隙结构的关系[J].南京林业大学学报,1998,22(4):23-27.
[13] Abdel-Nasser A, El-Hendawy. Influence of HNO₃oxidation on the structure and adsorptive properties of corncob-based activated carbon[J]. Carbon, 2003,41(4): 713-722.
[14] 范延臻,王宝贞,王琳,等.改性活性炭对有机物的吸附性能[J],环境化学,2001,20(5):444-448.
[15] Figueiredo J L, Pereira M F R, Freitas M M A, et al. Modification of the surface chemistry of activated carbons [J]. Carbon, 1999, 37(9): 1379-1389.

Related Articles 9

[1]	MAO Haiyan, ZHOU Dingguo, Zaher Hashisho, WANG Sunguo, CHEN Heng. Regeneration of activated carbon loaded with toluene using low temperature microwave and conductive heating methods [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2014, 38(06): 141-145.
[2]	ZHANG Wenbiao1, QIAN Xinbiao2, MA Lingfei1. Adsorption properties of bamboo charcoal under different carbonized temperatures for heavy metal ions [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2009, 33(06): 20-.
[3]	WU Guangqian, ZHANG Qisheng,*, ZHOU Peiguo, ZHOU Jianbin, CHEN Fangjie. Biodegradation of typical pollutants in wastewater by using immobilized microorganism bamboo charcoal [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2009, 33(01): 20-24.
[4]	ZHOU Jian-bin1, DENG Cong-jing1,FU Jin-he2 ,ZHANG Qi-sheng3*. Adsorption and degradation of benzene in atmosphere by Nano- TiO2 modified bamboo charcoal [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2008, 32(06): 5-8.
[5]	ZUO Song-lin, TENG Yong-sheng. Effects of technological parameters on the adsorption properties of activated carbons from petroleum coke by KOH activation [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2008, 32(03): 48-52.
[6]	SHI Yu-ting1, CHRUSCIEL L.2, ZOULALIAN A.2, ZHOU Ding-guo1*. Study on Conversion Ratio of Different Wood Species Into Charcoal [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2007, 31(04): 65-68.
[7]	XIE Hui1, LU Zhong-yi1, ZHOU Yong-hong2. The Catalysis of Activated Carbon Supported Heteropoly-acid for Terpinyl Acetate Synthesis [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2005, 29(06): 65-68.
[8]	ZHOU Jianbin,ZHANG Qisheng,GAO Shangyu. A Study on Preparation of Activated Carbon for Refinement of Pharmaceuticals from Hydrolysis Lignin [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 2003, 27(05): 40-42.
[9]	Zhou Jianbin\ Gao Shangyu\ Hu Chengwen\ Zuo Songlin\ Liu Qiming (College of Chemical Engineering Nanjing Forestry University\ Nanjing\ 210037). A Study on the Activated Carbon Composite Material of Gas Adsorption [J]. JOURNAL OF NANJING FORESTRY UNIVERSITY, 1999, 23(06): 43-46.

Metrics

Comments

www.nldxb.njfu.edu.cn

Edited ＆ Published by Editorial Department of Nanjing Forestry University(Natural Sciences Edition)
Address： No.159 Longpan Road,Nanjing 210037 Jiangsu,P.R.China
E-mail ：xuebao@njfu.edu.cn , xuebao@njfu.com.cn
Telephone +86-25-85428247,85427076
Distributed by China International Book Trading Corporation P.O. Box 399, Beijing ,P.R. China

Study on the characteristics of bamboo charcoal modified with nitric acid

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 9

Recommended Articles 0

Metrics

Comments

Author

Reader

Reviewer