Physical mechanical properties and nature durability of Bambusa emeiensis  bamboo scrimber of different ages

WEI Wanshu， QIN Daochun*

JOURNAL OF NANJING FORESTRY UNIVERSITY ›› 2011, Vol. 35 ›› Issue (06) : 111-115.

PDF(1352879 KB)
南京林业大学学报（自然科学版）
PDF(1352879 KB)
JOURNAL OF NANJING FORESTRY UNIVERSITY ›› 2011, Vol. 35 ›› Issue (06) : 111-115. DOI: 10.3969/j.jssn.1000-2006.2011.06.023

Physical mechanical properties and nature durability of Bambusa emeiensis  bamboo scrimber of different ages

  • WEI Wanshu1,2， QIN Daochun1*
Author information +
History +

Abstract

Bambusa emeiensis of 1 to 6yearold was as the raw material and phenol formaldehyde resin(PF) was as the adhesive to prepare bamboo scrimber. The influences of bamboos age on physical mechanical, natural decay resistance and mould inhibitor properties of bamboo scrimber were investigated. The results showed that the basic density increased with the increment age; mechanical properties strengthened with the increasing age, but it didnt change much; natural decay resistance of Bambusa emeiensis bamboo scrimber reached to the high antidecay level, while bamboo age had not significant influences on the natural decay resistance; all the 1 to 6yearsold bamboo scrimber test materials entire surface were inspected for mold growth after 4 weeks. This phenomenon showed that untreated bamboo scrimber was more prone to mildew and bamboo age had not significant influences on the natural moldresistant performance of bamboo scrimber. Based on comprehensive consideration of the physica mechanical and nature durability properties, in bamboo forest cultivation, Bambusa emeiensis as a kind of structural material appropriate cutting age should be 3 to 4yearold. 

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations
WEI Wanshu， QIN Daochun*. Physical mechanical properties and nature durability of Bambusa emeiensis  bamboo scrimber of different ages[J]. JOURNAL OF NANJING FORESTRY UNIVERSITY. 2011, 35(06): 111-115 https://doi.org/10.3969/j.jssn.1000-2006.2011.06.023

References

[1]易同培.四川竹类植物志[M].北京:中国林业出版社，1997.
[2]中国科学院植物研究所.中国高等植物图鉴:第5册[M].北京:科学出版社,1976.
[3]耿以理.中国主要植物图说——禾本科[M].北京:科学出版社,1959.
[4]李琴,汪奎宏.重组竹产业化发展可行性分析[J].木材工业，2007，21(1)：33-35.
[5]金菊婉,董诗文,李燕民,等.硼酸锌防腐处理对杨木定向刨花板性能的影响[J].南京林业大学学报:自然科学版，2009,33(5):81-85.
[6]Liese W, Weiner G. Ageing of bamboo culsm:A review[J]. Wood Science and Technology， 1996，30（2): 77-89.
[7]周芳纯.竹类培育学[M].北京:中国林业出版社,1998.
[8]张齐生,关明杰,纪文兰.毛竹材质生成过程中化学成分的变化[J].南京林业大学学报:自然科学版,2002,26(2):7-10.
[9]董敦义,关明杰,朱一辛,等.不同竹龄毛竹硬度的测试分析[J].林业科技开发,2009,23(5):48-50.
[10]俞友明,方伟,杨云芳,等.不同立地条件红壳竹竹材物理力学性质的比较[J].浙江林学院学报,2001,18(4):380-383.
[11]陈友地.十种竹材化学成分的研究[J].林产化学与工业,1985,5(4):30-39.
[12]Fengel D, Shao X. Studies on the lignin of the bamboo species Phyllostachys makino Hay[J]. Wood Science and Technology, 1984, 18: 103-112.
[13]Itoh T. Lignification of bamboo(Phyllostachys heterocycla Mitf.) during its growth[J]. Holzforschung, 1990, 44: 191-200.
[14]Higuchi T, Kimura N, Kawamura I. Differences of chemical properties of lignin of vascular bundles and of parenchymacells of bamboos[J]. Mokuzai Cakkaishi, 1966, 12: 173-178.
[15]王文久,辉朝茂,文翠.云南14种主要材用竹化学成分研究[J].竹子研究汇刊,1999,18(2):74-78.
[16]郑蓉.不同海拔毛竹竹材化学组成成分分析[J].浙江林业科技,2001,21(1):55-56.
[17]国家技术监督局.GB/T 15780—1995竹材物理力学性质试验方法[S].北京：中国标准出版社,1995.
[18]马灵飞,韩红,马乃训.部分散生竹材纤维形态及主要理化性能[J].浙江林学院学报,1993,10(4):361-367.
[19]中国林业科学研究院木材工业研究所.GB/T 20241—2006单板层级材[S].北京:中国标准出版社,2006.
[20]中国林业科学研究院林材工业研究所.GB/T 17657—1999人造板及饰面人造板理化性能试验方法[S].北京:中国标准出版社,1999.
[21]中国林业科学研究院木材工业研究所,广东省林业科学研究院.GB/T 13942.1—2009木材天然耐久性试验方法—天然耐腐性实验室试验方法[S].北京:中国标准出版社,2009.
[22]中国林业科学研究院热带林业研究所,中国林业科学研究院木材工业研究所.GB/T 18261—2000防霉剂防治木材霉菌及蓝变菌的试验[S].北京:中国标准出版社,2000.
[23]Curling S F, Murphy R J. The effect of artificial ageing on the durability of woodbased board materials against basidiomycete decay fungi[J]. Wood Science and Technology, 1999, 33(4): 245-257.
[24]Laks P E, Richter D L, Larkin G M. Biological deterioration of woodbase composite panels[J]. Wood Design Focus, 2000, 11 (4): 7-11.
[25]吴炳生,夏玉芳，张家贤，等.料慈竹化学成分的研究[J].浙江林学院学报,1955,12(3):281-285.
PDF(1352879 KB)

Accesses

Citation

Detail
Sections
Recommended
The full text is translated into English by AI, aiming to facilitate reading and comprehension. The core content is subject to the explanation in Chinese.

Author

Reader

Reviewer

www.nldxb.njfu.edu.cn

Edited ＆ Published by Editorial Department of Nanjing Forestry University(Natural Sciences Edition)
Address： No.159 Longpan Road,Nanjing 210037 Jiangsu,P.R.China
E-mail ：xuebao@njfu.edu.cn , xuebao@njfu.com.cn
Telephone +86-25-85428247,85427076
Distributed by China International Book Trading Corporation P.O. Box 399, Beijing ,P.R. China

/

〈 〉