Modification research of cellulose based urea-formaldehyde resin molding compound

LIU Juan, NAN Jingya, WANG Chunpeng, CHU Fuxiang, CHEN Riqing1, 2*

Journal of Nanjing Forestry University (Natural Sciences Edition） ›› 2015, Vol. 39 ›› Issue (04) : 127-131.

PDF(1947176 KB)
南京林业大学学报（自然科学版）
PDF(1947176 KB)
Journal of Nanjing Forestry University (Natural Sciences Edition） ›› 2015, Vol. 39 ›› Issue (04) : 127-131. DOI: 10.3969/j.issn.1000-2006.2015.04.022

Modification research of cellulose based urea-formaldehyde resin molding compound

  • LIU Juan1, NAN Jingya1, WANG Chunpeng1, 2, CHU Fuxiang3, CHEN Riqing1, 2*
Author information +
History +

Abstract

The effects of modifiers polyvinyl butyral, polyacrylate and polystyrene on size stability, mechanical properties and thermal stability of moulding compound were investigated, and the dynamic mechanical properties and microstructure of fracture surface of modified systems were studied with dynamic mechanical analysis(DMA)and scanning electron microscope(SEM). The results showed that moulding plastic had the best dimension stability when polyvinyl butyral, polyacrylate and polystyrene were added 20%, 20% and 10%, respectively. The impact strength and bending strength of urea-formaldehyde resin molding plastic modified with 20% polyvinyl butyral were 2.55 kJ/m2 and 88.3 MPa respectively, and increased by 49.1% and 63.2% comparing with unmodified compound. Polyacrylate could improve the low temperature resistance of molding compound, and moulding compound modified with polyvinyl butyral had good high-temperature performance; The DMA test results showed that polyvinyl butyral and polyacrylate had the toughening effects on the moulding compound, and the compatibility with urea-formaldehyde resin was better. The moulding compound modified with polystyrene could not be toughened. In addition, fracture surface of moulding compound modified with polyvinyl butyral and polyacrylate appeared gliding fracture and the compound modified with polystyrene appeared brittle fracture.

Cite this article

EndNote

Ris (Procite)

Bibtex

Download Citations
LIU Juan, NAN Jingya, WANG Chunpeng, CHU Fuxiang, CHEN Riqing1, 2*. Modification research of cellulose based urea-formaldehyde resin molding compound[J]. Journal of Nanjing Forestry University (Natural Sciences Edition）. 2015, 39(04): 127-131 https://doi.org/10.3969/j.issn.1000-2006.2015.04.022

References

[1] Roumeli E, Papadopoulou E, Pavlidou E, et al. Synthesis, characterization and thermal analysis of urea-formaldehyde/nano SiO2 resins [J].Thermochimica Acta, 2012(527):33-39.
[2] Gao Z H, Wang X M, Wan H, et al.Curing characteristics of urea-formaldehyde resin in the presence of various amounts of wood extracts and catalysts[J].Journal of Applied Polymer Science, 2008, 107(3):1555-1562.
[3] 关琦,杨小燕,许宁,等.氨基模塑料冲击性能研究[J].工程塑料应用,2011,39(7):18-21. Guan Q, Yang X Y, Xu N, et al. Study on impact strength of amino moulding plastic [J]. Engineering Plastics Application, 2011,39(7):18-21.
[4] 储富祥,王春鹏,金铁铃,等. 三聚氰胺甲醛模塑料的制备方法:中国, 200910033562.5[P].2009-06-23.
[5] Martin Kohlmay, Gerhard Zuckerstatter, Andreas Kandelbauer. Modification of melamine-formaldehyde resins by substances from renewable resources [J]. Journal of Applied Polymer Science, 2012, 124(6):4416-4423.
[6] 詹茂盛,董绪超,肖和平,等. 一种新型低收缩率氨基模塑料及其制备方法:中国, 201010186569.3[P]. 2010-05-12.
[7] 温明宇,时君友.新型有机硅改性低毒脲醛树脂的初步研究[J].林产工业,2009,36(5):38-40. Wen M Y, Shi J Y. Investigation on low toxic UF resin modified with a new type of silicone[J]. China Forest Products Industry, 2009, 36(5):38-40.
[8] 赵洪凯,王洪杰,赵广宇.丙烯酸酯改性不饱和聚酯的研究[J].广州化工,2012,40(3):63-66. Zhao H K, Wang H J, Zhao G Y. Research on unsaturated polyester resin modified by acrylate[J].Guangzhou Chemical Industry, 2012,40(3):63-66.
[9] 许宁,关琦,杨涛,等.氨基模塑料耐电击穿和耐冲击性能研究[J].塑料工业,2011,39(9):24-27. Xu N, Guan Q, Yang T, et al. Study on the dielectric breakdown and impact resistance of ammonia plastic mould[J]. China Plastic Industry, 2011,39(9):24-27.
[10] Suzana Samarija-Jovanovic’,Vojislav Jovanovic’,Sandra Konstantinovic’, et al. Thermal behavior of modified urea-formaldehyde resins[J]. J Therm Anal Calorim,2011,104(3):1159-1166.
[11] 韩春国,李守海,王春鹏,等. 增塑剂对脲醛树脂模塑料性能的影响[J].现代化工, 2011,31(2): 61-63. Han C G, Li S H, Wang C P, et al. Effects of different plasticizers oil performance of urea-formaldehyde moulding plastics[J]. Modern Chemical Industry, 2011,31(2): 61-63.
[12] 宋晓丽,陈莹,许玉芝,等.聚丙烯酸酯微球的制备及其增韧聚乳酸的研究[J].林产化学与工业,2014,34(3):60-64.Song X L, Chen Y, Xu Y Z, et al. Preparation of polyacrylate microsphere and its application in toughening of polylactic acid[J]. Chemistry and Industry of Forest Products, 2014,34(3):60-64.
[13] 肖鑫,谭正德,黄先威,等.改性纯丙乳液的制备[J].湖南工程学院学报:自然科学版, 2002,12(4):63-65.Xiao X, Tan Z D, Huang X W, et al. Preparation of modified pure acrylic emulsion[J].Journal of Hunan Institute of Engineering:Natural Sciences Edition, 2002,12(4):63-65.
[14] Liu J, Nan J Y, Wang C P, et al. Orthogonal experimental study on moulding conditions of amino moulding plastic[J]. Advanced Materials Research, 2014,900:596-600.
[15] 王威岗,韦杰,董长青.木质纤维热解的热重和反应动力学研究[J].可再生能源,2007,25(5):23-26.Wang W G, Wei J, Dong C Q. Thermogravimetric and thermokinetic study on pyrolysis of cellulose [J]. Renewable Energy Resources, 2007, 25(5):23-26.
[16] 雷海芬,王鹏,张英民,等.聚乙二醇增塑PLA/La-OMMT纳米复合材料的制备及性能研究[J].材料科学与工艺,2009,17(4):457-461.Lei H F, Wang P, Zhang Y M, et al. Preparation and properties of plasticized poly(lactic acid)nano-composite with modified organo-montmorillonites[J]. Materials Science & Technology, 2009,17(4):457-461.
PDF(1947176 KB)

Accesses

Citation

Detail
Sections
Recommended
The full text is translated into English by AI, aiming to facilitate reading and comprehension. The core content is subject to the explanation in Chinese.

Author

Reader

Reviewer

www.nldxb.njfu.edu.cn

Edited ＆ Published by Editorial Department of Nanjing Forestry University(Natural Sciences Edition)
Address： No.159 Longpan Road,Nanjing 210037 Jiangsu,P.R.China
E-mail ：xuebao@njfu.edu.cn , xuebao@njfu.com.cn
Telephone +86-25-85428247,85427076
Distributed by China International Book Trading Corporation P.O. Box 399, Beijing ,P.R. China

/

〈 〉